metallurgical bond

美 [ˌmetlˈɜːrdʒɪkl bɑːnd]英 [ˌmetəˈlɜːdʒɪkl bɒnd]
  • 网络冶金结合;冶金接合;冶金复合
metallurgical bondmetallurgical bond
  1. Though the thickness of coating is not even , metallurgical bond between coating and matrix is realized .

    涂层的厚度不均匀,但涂层与基体实现了冶金结合。

  2. The experiment results show that the connection of cemented carbide-manganese steel is metallurgical bond .

    硬质合金与基体结合较好,为冶金结合。

  3. The results show that the composite coatings have better metallurgical bond to the substrate , both crack and air hole are not found .

    结果显示,合金层与基体成良好的无裂纹气孔的冶金结合。

  4. The result shows that the bond between surfacing weld and base metal is metallurgical bond , and bond line is clear .

    结果表明,喷焊层与基体是冶金结合,结合线清晰。

  5. The results show that the metallurgical bond of brass and steel can be achieved by the process of cold - drawn and diffusion annealing ;

    结果表明,通过扩散复合可使黄铜/钢界面实现良好的冶金结合;

  6. The interface between coating and matrix of the composite is metallurgical bond , and their matching performances are excellent and each performance advantage is developed .

    该复合材料界面呈冶金结合,性能匹配良好,发挥了各自的使用性能与工艺性能优势。

  7. The bond between the coating and the carbon / carbon composite is mainly metallurgical bond , and mechanical bond , so the bonding strength is high .

    涂层与基体的结合主要以化学结合为主,并有机械结合,结合强度高。

  8. The method has some excellent characters , such as low voltage , fine and close texture , metallurgical bond with the substrate , suitable to various metal materials .

    该方法具有放电电压低、陶瓷层结构致密、与基体冶金结合、适用于多种金属材料等优点。

  9. The white-bright band , appearing between the coating and the substrate , proved metallurgical bond . Some defects appeared in the coating .

    表面冶金区与基体之间则存在白亮带,它是以平面晶的生长形态沿热流方向生长出来的,白亮层的形成表明涂层与基体实现了良好的冶金结合。

  10. The high strength originates from interaction between the two kinds of atoms existing at the interface , i.e.a direct metallurgical bond unperturbed but metallurgical defects .

    检验结果表明,高强结合是由于存在于界面的金属原子间作用力起到了实质性作用。

  11. The distribution of TiC particles was dispersive in titanium matrix . The microstructure was homogeneous and the interfaces between TiC particles and titanium matrix were metallurgical bond .

    显微组织显示了TiC颗粒弥散分布,复合材料组织均匀,TiC和基体冶金结合,界面较小。

  12. The manufacturing technologies of the steel aluminum composite conductor rail in the world can be classified into three categories , namely mechanical bond , mechanical / metallurgical bond and metallurgical bond .

    世界上钢铝复合导电轨制造技术,可归纳为机械结合、机械/冶金结合、冶金结合三大类。

  13. The experimental results show that the coating consists of γ - Fe single phase , there is a good metallurgical bond between coating and substrate , and the coating is free of crack and pore defect .

    试验结果表明,涂层由单相奥氏体组成,涂层与基体形成了良好的冶金结合,无裂纹、气孔等缺陷;

  14. The microstructure of medium manganese Fe-based alloy laser cladding coating is dense , and the coating and the substrate is metallurgical bond . The cladding coating has good property of hardness , wear resistance and contact fatigue resistance .

    制备的中锰铁基合金熔覆层组织致密,涂层与基体呈冶金结合,熔覆层硬度较高、具有较好的耐磨和抗接触疲劳性能。

  15. Using high carbon ferro-chrome and ferrovanadium as precursor , M7C3 + VC reinforced Fe-based hardfacing layers were produced by plasma arc cladding . A good metallurgical bond is obtained between the hardfacing layer and the substrate .

    利用高碳铬铁+钒铁作为预置粉末,采用等离子堆焊制备了M7C3+VC增强铁基堆焊层,所得Fe-Cr-V-C复合堆焊层同基体形成良好的冶金结合。

  16. The proportion of tensile-shear strength to tensile strength of the titanium is 0.6 ~ 0.7 . The high strength originates from interaction between the two kinds of atoms existing at the interface , i. e. a direct metallurgical bond unperturbed but metallurgical defects .

    拉剪强度与钛的拉伸强度比值为0.6~0.7。检验结果表明,高强结合是由于存在于界面的金属原子间作用力起到了实质性作用。

  17. The results show that the metallurgical bond of cladding and base metal is carried out with CMT technology . When wire feeding speed ( vs ) is 5.0 m / min and welding speed is 17 mm / s , the rate of dilution is extremely low .

    结果表明,CMT技术实现了熔敷层与基体的冶金结合,送丝速度为5.0m/min,焊接速度为17.0mm/s时,稀释率极低;

  18. The experiment results show that the connection zone may be divided into multicomponent eutectoid , tungsten carbide and narrow ferrite and the interface is found to be a metallurgical bond because of the element diffusion , metallurgy reaction and formation of the new compound phase during the cast-in process .

    实验结果表明:结合层是由窄小的铁素体带和多元共析体+条块状WC组成,界面元素发生扩散及冶金反应并有新相产生,呈典型的冶金结合。